MARS-26-0407 Inspected
Fastener pull-through specimens. Linked through ION run records to print, oven, furnace, inspection and image data.
Material systemC/SiC (PIP)
Layup0/45/90/-45 x4
Fiber lotT700-2609-49
Resin lotRS-56D
Printed09/04/2026 20:38
Printed mass124.31 g
PIP cycles done5, mass gain 40.9%
Current stepDimensional inspection
Process history (ION)
| # | Procedure | Completed | Operator | Recorded values |
|---|---|---|---|---|
| 1 | CF3D Print RUN-18950 |
09/05/2026 00:18 | Marisol Vega | Print job ID: J-26-0407, Program: Fastener pull-through specimens, Material system: C/SiC (PIP), Layup: 0/45/90/-45 x4, Fiber lot: T700-2609-49, Resin lot: RS-56D, Printed mass (g): 124.31 |
| 2 | Grieve Oven Operation RUN-18951 |
09/06/2026 16:23 | Marisol Vega | Oven program: Post-cure 177C, Cycle start: 2026-09-06T08:18 |
| 3 | Polymer Infiltration and Pyrolysis Cycle RUN-18952 |
09/09/2026 14:48 | Marisol Vega | Cycle number: 1, Mass before infiltration (g): 124.31, Mass after pyrolysis (g): 145.16, Precursor: SMP-10 |
| 4 | GCF Furnace Operation RUN-18955 |
09/09/2026 14:48 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0407-1, Peak setpoint (C): 1200 |
| 5 | Polymer Infiltration and Pyrolysis Cycle RUN-18957 |
09/11/2026 20:26 | Marisol Vega | Cycle number: 2, Mass before infiltration (g): 145.16, Mass after pyrolysis (g): 159.97, Precursor: SMP-10 |
| 6 | GCF Furnace Operation RUN-18958 |
09/11/2026 20:26 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0407-2, Peak setpoint (C): 1000 |
| 7 | Polymer Infiltration and Pyrolysis Cycle RUN-18959 |
09/14/2026 04:30 | Marisol Vega | Cycle number: 3, Mass before infiltration (g): 159.97, Mass after pyrolysis (g): 168.39, Precursor: SMP-10 |
| 8 | GCF Furnace Operation RUN-18961 |
09/14/2026 04:30 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0407-3, Peak setpoint (C): 1000 |
| 9 | Polymer Infiltration and Pyrolysis Cycle RUN-18963 |
09/15/2026 19:43 | Marisol Vega | Cycle number: 4, Mass before infiltration (g): 168.39, Mass after pyrolysis (g): 172.83, Precursor: SMP-10 |
| 10 | GCF Furnace Operation RUN-18966 |
09/15/2026 19:43 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0407-4, Peak setpoint (C): 1000 |
| 11 | Polymer Infiltration and Pyrolysis Cycle RUN-18967 |
09/17/2026 16:43 | Marisol Vega | Cycle number: 5, Mass before infiltration (g): 172.83, Mass after pyrolysis (g): 175.14, Precursor: SMP-10 |
| 12 | GCF Furnace Operation RUN-18969 |
09/17/2026 16:43 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0407-5, Peak setpoint (C): 1000 |
| 13 | Surface grind a-bars RUN-18972 |
09/19/2026 22:16 | Marisol Vega | A-bars cut: 5, Grind wheel: Diamond 120 grit |
| 14 | Dimensional inspection RUN-21798 |
09/20/2026 13:51 | Marisol Vega | CMM report exported: Yes, Program: MARS_ABAR_V2 |
Densification by PIP cycle
Print job
| Job | Machine | Layers | Avg tow tension (N) | Fault events |
|---|---|---|---|---|
| J-26-0407 | CF3D Robot | 8 | 19.68 | 1 |
Oven and furnace cycles
| Cycle | Machine | Started | Peak setpoint (C) | Max soak dev. (C) | Result |
|---|---|---|---|---|---|
| GO-RUN-18951 | Grieve Oven | 09/06/2026 08:18 | 177.0 | 1.80 | Within tolerance |
| GCF-S-0407-1 | Small GCF | 09/09/2026 00:55 | 1,200.0 | 5.00 | Within tolerance |
| GCF-S-0407-2 | Small GCF | 09/11/2026 06:13 | 1,000.0 | 4.80 | Within tolerance |
| GCF-S-0407-3 | Small GCF | 09/13/2026 14:38 | 1,000.0 | 3.80 | Within tolerance |
| GCF-S-0407-4 | Small GCF | 09/15/2026 03:50 | 1,000.0 | 5.00 | Within tolerance |
| GCF-S-0407-5 | Small GCF | 09/17/2026 02:49 | 1,000.0 | 4.30 | Within tolerance |
Inspection
| Feature | Characteristic | Nominal | Measured | Tolerance | Deviation | Result |
|---|---|---|---|---|---|---|
| LENGTH | Distance | 152.4000 | 152.4061 | 0.2500 | 0.0061 | Within tolerance |
| WIDTH | Distance | 25.4000 | 25.3461 | 0.1500 | -0.0539 | Within tolerance |
| THK_1 | Thickness | 4.8000 | 4.9067 | 0.2000 | 0.1067 | Within tolerance |
| THK_2 | Thickness | 4.8000 | 4.6439 | 0.2000 | -0.1561 | Within tolerance |
| THK_3 | Thickness | 4.8000 | 4.7759 | 0.2000 | -0.0241 | Within tolerance |
| FLAT_TOP | Flatness | 0.0000 | 0.0023 | 0.1000 | 0.0023 | Within tolerance |
| HOLE_1 | Diameter | 6.3500 | 6.3412 | 0.0500 | -0.0088 | Within tolerance |
| HOLE_2 | Diameter | 6.3500 | 6.3646 | 0.0500 | 0.0146 | Within tolerance |
CMM report MARS-26-0407_20260920_1316.csv, inspected 09/20/2026 13:16
| Region | Sa (um) | Sq (um) | Sz (um) | Sdr % |
|---|---|---|---|---|
| Top face | 3.635 | 4.616 | 31.18 | 1.88 |
| Edge | 2.961 | 3.760 | 22.34 | 2.64 |
| Bottom face | 2.884 | 3.663 | 28.72 | 3.99 |
Height map, optical profilometer. Image stored in blob storage.
Images
Digital Optical Microscope, 200xCross-section A, 09/20/2026 14:16
Digital Optical Microscope, 200xCross-section B, 09/20/2026 14:26
SEM, 500xas-ground edge, 09/20/2026 16:16
SEM, 2500xas-ground edge, 09/20/2026 16:28
Data as of pipeline run R-20261105-0200, finished 11/05/2026 02:00 Mountain. Tables: mars.gold and mars.ops.