Overview / Parts / MARS-26-0410

MARS-26-0410 Inspected

Hot structure panel. Linked through ION run records to print, oven, furnace, inspection and image data.

Material systemC/C (phenolic, reinfiltrated)

Layup0/60/-60 x6

Fiber lotT700-2610-82

Resin lotRS-43A

Printed09/09/2026 08:03

Printed mass72.43 g

PIP cycles done3, mass gain 23.5%

Current stepDimensional inspection

Process history (ION)

#	Procedure	Completed	Operator	Recorded values
1	CF3D Print RUN-19017	09/09/2026 10:33	Marisol Vega	Print job ID: J-26-0410, Program: Hot structure panel, Material system: C/C (phenolic, reinfiltrated), Layup: 0/60/-60 x6, Fiber lot: T700-2610-82, Resin lot: RS-43A, Printed mass (g): 72.43
2	Grieve Oven Operation RUN-19020	09/10/2026 15:34	Marisol Vega	Oven program: Post-cure 177C, Cycle start: 2026-09-10T07:33
3	Polymer Infiltration and Pyrolysis Cycle RUN-19022	09/12/2026 21:28	Marisol Vega	Cycle number: 1, Mass before infiltration (g): 72.43, Mass after pyrolysis (g): 81.82, Precursor: Furfuryl alcohol
4	GCF Furnace Operation RUN-19025	09/12/2026 21:28	Marisol Vega	Furnace: Small GCF, Furnace cycle ID: GCF-S-0410-1, Peak setpoint (C): 1200
5	Polymer Infiltration and Pyrolysis Cycle RUN-19028	09/15/2026 13:16	Marisol Vega	Cycle number: 2, Mass before infiltration (g): 81.82, Mass after pyrolysis (g): 86.37, Precursor: Furfuryl alcohol
6	GCF Furnace Operation RUN-19030	09/15/2026 13:16	Marisol Vega	Furnace: Small GCF, Furnace cycle ID: GCF-S-0410-2, Peak setpoint (C): 1000
7	Polymer Infiltration and Pyrolysis Cycle RUN-19031	09/17/2026 21:35	Marisol Vega	Cycle number: 3, Mass before infiltration (g): 86.37, Mass after pyrolysis (g): 89.44, Precursor: Furfuryl alcohol
8	GCF Furnace Operation RUN-19032	09/17/2026 21:35	Marisol Vega	Furnace: Small GCF, Furnace cycle ID: GCF-S-0410-3, Peak setpoint (C): 1000
9	Surface grind a-bars RUN-19034	09/20/2026 00:59	Marisol Vega	A-bars cut: 3, Grind wheel: Diamond 120 grit
10	Dimensional inspection RUN-25460	09/21/2026 01:34	Marisol Vega	CMM report exported: Yes, Program: MARS_ABAR_V2

Densification by PIP cycle

Print job

Job	Machine	Layers	Avg tow tension (N)	Fault events
J-26-0410	CF3D Robot	16	19.28	1

Oven and furnace cycles

Cycle	Machine	Started	Peak setpoint (C)	Max soak dev. (C)	Result
GO-RUN-19020	Grieve Oven	09/10/2026 07:33	177.0	1.70	Within tolerance
GCF-S-0410-1	Small GCF	09/12/2026 07:09	1,200.0	4.40	Within tolerance
GCF-S-0410-2	Small GCF	09/14/2026 19:29	1,000.0	5.00	Within tolerance
GCF-S-0410-3	Small GCF	09/17/2026 06:46	1,000.0	4.60	Within tolerance

Inspection

Feature	Characteristic	Nominal	Measured	Tolerance	Deviation	Result
LENGTH	Distance	152.4000	152.3626	0.2500	-0.0374	Within tolerance
WIDTH	Distance	25.4000	25.5085	0.1500	0.1085	Within tolerance
THK_1	Thickness	4.8000	4.8167	0.2000	0.0167	Within tolerance
THK_2	Thickness	4.8000	4.7628	0.2000	-0.0372	Within tolerance
THK_3	Thickness	4.8000	4.7207	0.2000	-0.0793	Within tolerance
FLAT_TOP	Flatness	0.0000	0.0021	0.1000	0.0021	Within tolerance
HOLE_1	Diameter	6.3500	6.3269	0.0500	-0.0231	Within tolerance
HOLE_2	Diameter	6.3500	6.3825	0.0500	0.0325	Within tolerance

CMM report MARS-26-0410_20260921_0059.csv, inspected 09/21/2026 00:59

Region	Sa (um)	Sq (um)	Sz (um)	Sdr %
Top face	1.739	2.209	13.76	6.24
Edge	1.356	1.722	14.04	3.54
Bottom face	1.550	1.969	16.46	6.74

Height map from the optical profilometer

Height map, optical profilometer. Image stored in blob storage.

Images

Digital Optical Microscope image of MARS-26-0410

Digital Optical Microscope, 200x
Cross-section C, 09/21/2026 01:59

Digital Optical Microscope, 200x
Cross-section C, 09/21/2026 02:09

Digital Optical Microscope, 200x
Cross-section A, 09/21/2026 02:19

SEM, 1000x
as-ground edge, 09/21/2026 03:59

SEM, 1000x
polished section, 09/21/2026 04:11

Data as of pipeline run R-20261105-0200, finished 11/05/2026 02:00 Mountain. Tables: mars.gold and mars.ops.