MARS-26-0433 In process
Leading edge coupons, C/SiC. Linked through ION run records to print, oven, furnace, inspection and image data.
Material systemC/SiC (PIP)
Layup0/45/90/-45 x4
Fiber lotT700-2607-23
Resin lotRS-49B
Printed10/18/2026 20:59
Printed mass133.83 g
PIP cycles done6, mass gain 44.6%
Current stepSurface grind a-bars
Process history (ION)
| # | Procedure | Completed | Operator | Recorded values |
|---|---|---|---|---|
| 1 | CF3D Print RUN-19456 |
10/19/2026 00:28 | Marisol Vega | Print job ID: J-26-0433, Program: Leading edge coupons, C/SiC, Material system: C/SiC (PIP), Layup: 0/45/90/-45 x4, Fiber lot: T700-2607-23, Resin lot: RS-49B, Printed mass (g): 133.83 |
| 2 | Grieve Oven Operation RUN-19458 |
10/20/2026 14:16 | Marisol Vega | Oven program: Post-cure 177C, Cycle start: 2026-10-20T05:42 |
| 3 | Polymer Infiltration and Pyrolysis Cycle RUN-19459 |
10/23/2026 14:40 | Marisol Vega | Cycle number: 1, Mass before infiltration (g): 133.83, Mass after pyrolysis (g): 159.31, Precursor: SMP-10 |
| 4 | GCF Furnace Operation RUN-19462 |
10/23/2026 14:40 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0433-1, Peak setpoint (C): 1200 |
| 5 | Polymer Infiltration and Pyrolysis Cycle RUN-19463 |
10/25/2026 13:14 | Marisol Vega | Cycle number: 2, Mass before infiltration (g): 159.31, Mass after pyrolysis (g): 175.61, Precursor: SMP-10 |
| 6 | GCF Furnace Operation RUN-19466 |
10/25/2026 13:14 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0433-2, Peak setpoint (C): 1000 |
| 7 | Polymer Infiltration and Pyrolysis Cycle RUN-19467 |
10/27/2026 09:24 | Marisol Vega | Cycle number: 3, Mass before infiltration (g): 175.61, Mass after pyrolysis (g): 184.01, Precursor: SMP-10 |
| 8 | GCF Furnace Operation RUN-19468 |
10/27/2026 09:24 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0433-3, Peak setpoint (C): 1000 |
| 9 | Polymer Infiltration and Pyrolysis Cycle RUN-19470 |
10/29/2026 11:45 | Marisol Vega | Cycle number: 4, Mass before infiltration (g): 184.01, Mass after pyrolysis (g): 189.5, Precursor: SMP-10 |
| 10 | GCF Furnace Operation RUN-19472 |
10/29/2026 11:45 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0433-4, Peak setpoint (C): 1000 |
| 11 | Polymer Infiltration and Pyrolysis Cycle RUN-19473 |
10/31/2026 19:55 | Marisol Vega | Cycle number: 5, Mass before infiltration (g): 189.5, Mass after pyrolysis (g): 191.99, Precursor: SMP-10 |
| 12 | GCF Furnace Operation RUN-19475 |
10/31/2026 19:55 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0433-5, Peak setpoint (C): 1000 |
| 13 | Polymer Infiltration and Pyrolysis Cycle RUN-19476 |
11/03/2026 12:53 | Marisol Vega | Cycle number: 6, Mass before infiltration (g): 191.99, Mass after pyrolysis (g): 193.54, Precursor: SMP-10 |
| 14 | GCF Furnace Operation RUN-19479 |
11/03/2026 12:53 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0433-6, Peak setpoint (C): 1000 |
| 15 | Surface grind a-bars RUN-19482 |
11/04/2026 16:32 | Marisol Vega | A-bars cut: 5, Grind wheel: Diamond 120 grit |
Densification by PIP cycle
Print job
| Job | Machine | Layers | Avg tow tension (N) | Fault events |
|---|---|---|---|---|
| J-26-0433 | CF3D Robot | 12 | 19.10 | 1 |
Oven and furnace cycles
| Cycle | Machine | Started | Peak setpoint (C) | Max soak dev. (C) | Result |
|---|---|---|---|---|---|
| GO-RUN-19458 | Grieve Oven | 10/20/2026 05:42 | 177.0 | 1.70 | Within tolerance |
| GCF-S-0433-1 | Small GCF | 10/22/2026 22:25 | 1,200.0 | 4.80 | Within tolerance |
| GCF-S-0433-2 | Small GCF | 10/24/2026 19:23 | 1,000.0 | 4.70 | Within tolerance |
| GCF-S-0433-3 | Small GCF | 10/26/2026 19:22 | 1,000.0 | 3.50 | Within tolerance |
| GCF-S-0433-4 | Small GCF | 10/28/2026 18:51 | 1,000.0 | 4.60 | Within tolerance |
| GCF-S-0433-5 | Small GCF | 10/31/2026 05:13 | 1,000.0 | 5.60 | Within tolerance |
| GCF-S-0433-6 | Small GCF | 11/02/2026 19:20 | 1,000.0 | 4.80 | Within tolerance |
Inspection
This part has not been inspected yet.