MARS-26-0427 Inspected
Fastener pull-through specimens. Linked through ION run records to print, oven, furnace, inspection and image data.
Material systemC/SiC (PIP)
Layup0 x16
Fiber lotT700-2610-17
Resin lotRS-55A
Printed10/09/2026 09:50
Printed mass101.42 g
PIP cycles done6, mass gain 42.5%
Current stepDimensional inspection
Process history (ION)
| # | Procedure | Completed | Operator | Recorded values |
|---|---|---|---|---|
| 1 | CF3D Print RUN-19340 |
10/09/2026 11:25 | Marisol Vega | Print job ID: J-26-0427, Program: Fastener pull-through specimens, Material system: C/SiC (PIP), Layup: 0 x16, Fiber lot: T700-2610-17, Resin lot: RS-55A, Printed mass (g): 101.42 |
| 2 | Grieve Oven Operation RUN-19341 |
10/10/2026 18:43 | Marisol Vega | Oven program: Post-cure 177C, Cycle start: 2026-10-10T10:25 |
| 3 | Polymer Infiltration and Pyrolysis Cycle RUN-19344 |
10/12/2026 21:11 | Marisol Vega | Cycle number: 1, Mass before infiltration (g): 101.42, Mass after pyrolysis (g): 119.89, Precursor: SMP-10 |
| 4 | GCF Furnace Operation RUN-19345 |
10/12/2026 21:11 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0427-1, Peak setpoint (C): 1200 |
| 5 | Polymer Infiltration and Pyrolysis Cycle RUN-19347 |
10/15/2026 12:00 | Marisol Vega | Cycle number: 2, Mass before infiltration (g): 119.89, Mass after pyrolysis (g): 131.42, Precursor: SMP-10 |
| 6 | GCF Furnace Operation RUN-19350 |
10/15/2026 12:00 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0427-2, Peak setpoint (C): 1000 |
| 7 | Polymer Infiltration and Pyrolysis Cycle RUN-19351 |
10/18/2026 05:29 | Marisol Vega | Cycle number: 3, Mass before infiltration (g): 131.42, Mass after pyrolysis (g): 137.92, Precursor: SMP-10 |
| 8 | GCF Furnace Operation RUN-19353 |
10/18/2026 05:29 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0427-3, Peak setpoint (C): 1000 |
| 9 | Polymer Infiltration and Pyrolysis Cycle RUN-19355 |
10/20/2026 14:38 | Marisol Vega | Cycle number: 4, Mass before infiltration (g): 137.92, Mass after pyrolysis (g): 141.5, Precursor: SMP-10 |
| 10 | GCF Furnace Operation RUN-19356 |
10/20/2026 14:38 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0427-4, Peak setpoint (C): 1000 |
| 11 | Polymer Infiltration and Pyrolysis Cycle RUN-19359 |
10/22/2026 19:01 | Marisol Vega | Cycle number: 5, Mass before infiltration (g): 141.5, Mass after pyrolysis (g): 143.5, Precursor: SMP-10 |
| 12 | GCF Furnace Operation RUN-19360 |
10/22/2026 19:01 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0427-5, Peak setpoint (C): 1000 |
| 13 | Polymer Infiltration and Pyrolysis Cycle RUN-19362 |
10/25/2026 00:31 | Marisol Vega | Cycle number: 6, Mass before infiltration (g): 143.5, Mass after pyrolysis (g): 144.54, Precursor: SMP-10 |
| 14 | GCF Furnace Operation RUN-19363 |
10/25/2026 00:31 | Marisol Vega | Furnace: Small GCF, Furnace cycle ID: GCF-S-0427-6, Peak setpoint (C): 1000 |
| 15 | Surface grind a-bars RUN-19365 |
10/27/2026 04:42 | Marisol Vega | A-bars cut: 5, Grind wheel: Diamond 120 grit |
| 16 | Dimensional inspection RUN-24057 |
10/28/2026 01:17 | Marisol Vega | CMM report exported: Yes, Program: MARS_ABAR_V2 |
Densification by PIP cycle
Print job
| Job | Machine | Layers | Avg tow tension (N) | Fault events |
|---|---|---|---|---|
| J-26-0427 | CF3D Robot | 9 | 17.81 | 1 |
Oven and furnace cycles
| Cycle | Machine | Started | Peak setpoint (C) | Max soak dev. (C) | Result |
|---|---|---|---|---|---|
| GO-RUN-19341 | Grieve Oven | 10/10/2026 10:25 | 177.0 | 1.20 | Within tolerance |
| GCF-S-0427-1 | Small GCF | 10/12/2026 05:22 | 1,200.0 | 6.30 | Within tolerance |
| GCF-S-0427-2 | Small GCF | 10/14/2026 20:49 | 1,000.0 | 4.00 | Within tolerance |
| GCF-S-0427-3 | Small GCF | 10/17/2026 15:00 | 1,000.0 | 5.50 | Within tolerance |
| GCF-S-0427-4 | Small GCF | 10/19/2026 22:10 | 1,000.0 | 5.70 | Within tolerance |
| GCF-S-0427-5 | Small GCF | 10/22/2026 02:12 | 1,000.0 | 4.40 | Within tolerance |
| GCF-S-0427-6 | Small GCF | 10/24/2026 11:14 | 1,000.0 | 4.60 | Within tolerance |
Inspection
| Feature | Characteristic | Nominal | Measured | Tolerance | Deviation | Result |
|---|---|---|---|---|---|---|
| LENGTH | Distance | 152.4000 | 152.2742 | 0.2500 | -0.1258 | Within tolerance |
| WIDTH | Distance | 25.4000 | 25.4298 | 0.1500 | 0.0298 | Within tolerance |
| THK_1 | Thickness | 4.8000 | 4.7484 | 0.2000 | -0.0516 | Within tolerance |
| THK_2 | Thickness | 4.8000 | 4.9558 | 0.2000 | 0.1558 | Within tolerance |
| THK_3 | Thickness | 4.8000 | 4.9266 | 0.2000 | 0.1266 | Within tolerance |
| FLAT_TOP | Flatness | 0.0000 | 0.0283 | 0.1000 | 0.0283 | Within tolerance |
| HOLE_1 | Diameter | 6.3500 | 6.3302 | 0.0500 | -0.0198 | Within tolerance |
| HOLE_2 | Diameter | 6.3500 | 6.3680 | 0.0500 | 0.0180 | Within tolerance |
CMM report MARS-26-0427_20261028_0042.csv, inspected 10/28/2026 00:42
| Region | Sa (um) | Sq (um) | Sz (um) | Sdr % |
|---|---|---|---|---|
| Top face | 3.196 | 4.059 | 24.56 | 6.67 |
| Edge | 2.574 | 3.270 | 26.73 | 6.28 |
| Bottom face | 3.096 | 3.932 | 33.07 | 2.80 |
Height map, optical profilometer. Image stored in blob storage.
Images
Digital Optical Microscope, 200xCross-section A, 10/28/2026 01:42
Digital Optical Microscope, 200xCross-section B, 10/28/2026 01:52
SEM, 2500xas-ground edge, 10/28/2026 03:42
Data as of pipeline run R-20261105-0200, finished 11/05/2026 02:00 Mountain. Tables: mars.gold and mars.ops.